Made of cross linked chlorinated polyolefin
Features
• Made of cross linked chlorinated polyolefin
• Resistant to most fluids and solvents, including aviation and ground-vehicle fuels, lubricating oil, and hydraulic fluids
• Good flexibility at low temperature
• Resistant to abrasion and physical abuse while providing flexibility and strain relief
• Performance meets requirements of SAE-AMS-DTL-23053/1.
• Widely used for insulation, strain relief, and abrasion protection on cable harnesses and wire bundles in the military and aerospace industries. Especially suitable for applications requiring exposure to fluids and solvents at elevated temperatures.
• RoHS compliant
• Operation temperature: -45°C to 105°C
• Shrink temperature: start at 90°C, and fully recovered at 130°C
• Standard color: Black.
| Technical Data | ||
| Property | Test Method | Typical Performance | |
| Tensile strength(MPa) | ASTM D 41 2 | ≥10.3 |
| Elongation at Break (%) | ASTM D 41 2 | ≥225% |
| Tensile stress at 200% elongation(MPa) | ASTM D 41 2 | ≤10.3 |
| Tensile Strength After Aging (120℃,168 hrs) (%) | SAE-AMS-DTL-23053 | ≥8.3 |
| Elongation at Break after Aging (120°C,168 hrs) (%) | SAE-AMS-DTL-23053 | ≥175% |
| Dielectric Strength (kV/mm) | ASTM D 2671 | ≥11.8 |
| Volume resistivity (Ω·cml | ASTM D 876 | ≥1×1011 |
| Flammability(Self extinguishing 15 seconds; 3 inches) | ASTM D2671, Procedure A | Pass |
| Fungus resistance | ASTM G 21 | No growth |
| Low temperature flexibility | -70°C,4 hrs | No cracking |
Features
• Made of cross linked chlorinated polyolefin
• Resistant to most fluids and solvents, including aviation and ground-vehicle fuels, lubricating oil, and hydraulic fluids
• Good flexibility at low temperature
• Resistant to abrasion and physical abuse while providing flexibility and strain relief
• Performance meets requirements of SAE-AMS-DTL-23053/1.
• Widely used for insulation, strain relief, and abrasion protection on cable harnesses and wire bundles in the military and aerospace industries. Especially suitable for applications requiring exposure to fluids and solvents at elevated temperatures.
• RoHS compliant
• Operation temperature: -45°C to 105°C
• Shrink temperature: start at 90°C, and fully recovered at 130°C
• Standard color: Black.
| Technical Data | ||
| Property | Test Method | Typical Performance | |
| Tensile strength(MPa) | ASTM D 41 2 | ≥10.3 |
| Elongation at Break (%) | ASTM D 41 2 | ≥225% |
| Tensile stress at 200% elongation(MPa) | ASTM D 41 2 | ≤10.3 |
| Tensile Strength After Aging (120℃,168 hrs) (%) | SAE-AMS-DTL-23053 | ≥8.3 |
| Elongation at Break after Aging (120°C,168 hrs) (%) | SAE-AMS-DTL-23053 | ≥175% |
| Dielectric Strength (kV/mm) | ASTM D 2671 | ≥11.8 |
| Volume resistivity (Ω·cml | ASTM D 876 | ≥1×1011 |
| Flammability(Self extinguishing 15 seconds; 3 inches) | ASTM D2671, Procedure A | Pass |
| Fungus resistance | ASTM G 21 | No growth |
| Low temperature flexibility | -70°C,4 hrs | No cracking |